Plasmon-free polymeric nanowrinkled substrates for surface-enhanced raman spectroscopy of two-dimensional materials
Article [Accepted Manuscript]
Is part of
Langmuir ; vol. 37, no. 1, pp. 322-329.Publisher(s)
American Chemical SocietyAuthor(s)
Affiliation
Abstract(s)
We report plasmon-free polymeric nanowrinkled substrates for surface-enhanced Raman spectroscopy (SERS). Our simple, rapid, and cost-effective fabrication method involves depositing a poly(ethylene glycol)diacrylate (PEGDA) prepolymer solution droplet on a fully polymerized, flat PEGDA substrate, followed by drying the droplet at room conditions and plasma treatment, which polymerizes the deposited layer. The thin polymer layer buckles under axial stress during plasma treatment due to its different mechanical properties from the underlying soft substrate, creating hierarchical wrinkled patterns. We demonstrate the variation of the wrinkling wavelength with the drying polymer molecular weight and concentration (direct relations are observed). A transition between micron to nanosized wrinkles is observed at 5 v % concentration of the lower molecular-weight polymer solution (PEGDA Mn 250). The wrinkled substrates are observed to be reproducible, stable (at room conditions), and, especially, homogeneous at and below the transition regime, where nanowrinkles dominate, making them suitable candidates for SERS. As a proof-of-concept, the enhanced SERS performance of micro/nanowrinkled surfaces in detecting graphene and hexagonal boron nitride (h-BN) is illustrated. Compared to the SiO2/Si surfaces, the wrinkled PEGDA substrates significantly enhanced the signature Raman band intensities of graphene and h-BN by a factor of 8 and 50, respectively.
Other location(s)
Collections
This document disseminated on Papyrus is the exclusive property of the copyright holders and is protected by the Copyright Act (R.S.C. 1985, c. C-42). It may be used for fair dealing and non-commercial purposes, for private study or research, criticism and review as provided by law. For any other use, written authorization from the copyright holders is required.